Q1: Proč je váš oxid zirkoničitý po slinování zelený?

A1:It is because your finance has been polluted, different types of zirconia have different subsidiary substances during production. when sintering the substance will get rid of zirconia and come to the heart of finance, it made the heart of finance was polluted because the substance doesn't get rid of completely.

Pls, sinter the finance empty immediately to help the substance get rid of completely. Each time sintering the heating elements will have new crystalline film. It is better to change the sintering tray and beads as well.

Tipy, jak se vyhnout znečištění:

1, Neslinujte průběžně různé druhy zirkonu.

Například dnes spékání bílých bloků, pokud zítra potřebujete sintrové předstínované bloky, měli byste slinovat finance prázdné po bílých blocích a poté sintrovat předstínované.

2, Všechny koruny bílých bloků by měly být sušeny 200 stupňů 30 minut před slinováním

Otázka 2: Jaký je rozdíl mezi SHT Multilayer a 3D-Plus Multilayer?

A2: SHT je barevný přechod. Pevnost je 1200 MPA a 45procentní průsvitnost.

3D-Plus je přechod barev i síly. Síla od 600 MPA do 900 MPA, průsvitnost od 43 procent do 49 procent.

Mezitím testujeme nový 3D E-Plus, síla může být max. 1100 a průsvitnost od 47 procent do 49 procent .

Q3: Pontinská zlomenina po zasklení?

A3: Tento problém má dvě možnosti:

1. The upper gingival porcelain requires repeated enamels, and the burned bridge undergoes multiple heating and cooling. Pulling and cracking are caused by the too fast cooling rate.
Suggestions: Lower the cooling rate and reduce the number of times porcelain loading

Porcelain furnace cooling program should be set a little slower, porcelain furnace cooling too fast will cause thermal stress, thermal shock, ceramics are most afraid of rapid cooling and heating, porcelain furnace cooling down a little bit, the lower temperature limit is set a little lower

This needs to be paid attention to in the porcelain furnace, the mouthful of rapid cold causes thermal stress cracking
Generally, the teeth in the porcelain furnace come out at 700 degree  and come into contact with the air, and the teeth at 700 degree  encounter the cold air at 25 degree , which causes cracking.
Easiest to break from the missing position, because the missing position is solid, accumulates more heat, and dissipates slowly

2. When the porcelain is cut, the teeth are cut vertically with fine slices. (In the past, metal teeth and porcelain teeth were cut in this way, so technicians are used to it).

Suggestion: When the car porcelain is cut between the teeth, it should be cut sideways in the direction of the teeth. However, this possibility is generally small.